Leonardo Pasaribu1, Ir. Tugiman, MT2

1,2 Jurusan Teknik Mesin Sekolah Tinggi Teknik Harapan Medan 2015

E-mail: leon810581@gmail.com

 

ABSTRAK

Kondisi hutan Indonesia menunjukkan produktivitas yang semakin menurun, padahal kebutuhan bahan baku kayu di masyarakat semakin meningkat. Hal ini dapat diatasi dengan cara pemanfaatan berbagai macam teknologi, seperti pengalihan pembuatan papan dari kayu solid menjadi papan partikel komposit polymeric foam serat alam enceng gondok. Pada penelitian ini, material komposit dibuat dengan memvariasikan kadar perekat resin 90%, 85% dan 80% dengan campuran isosianat dan poliol 5%, 5%, 5%. Penelitian ini bertujuan untuk memperoleh nilai ketangguhan pada spesimen komposit polymeric foam serbuk dan serat enceng gondok, mendapatkan perilaku mekanis, mengetahui pengaruh komposisi bahan dengan melakukan pengujian impak standart ASTM E23-56T dan mendapatkan komposisi bahan terbaik untuk dijadikan material komposit polymeric foam. Hasil pengujian impak dengan metode charpy menunjukkan bahwa nilai ketangguhan spesimen tertinggi yang diperoleh adalah 110.8 J/mm2, perilaku mekanis ditunjukkan dengan terjadinya perpatahan pada spesimen akibat benturan pendulum saat pengujian, komposisi bahan sangat mempengaruhi nilai ketangguhan spesimen komposit dan komposisi bahan terbaik untuk dijadikan material komposit adalah serbuk enceng gondok dengan kadar perekat resin 90%.

Kata kunci : serat/serbuk eceng gondok, komposit polymeric, uji impak.

ABSTRAK

Indonesian forest conditions showed productivity declining, whereas the need for wood raw material in the community is increasing. This can be overcome by the use of various technologies, such as the transfer of the manufacture of solid wood boards into particle board polymeric foam composite of natural fibers of water hyacinth. In this study, a composite material made with varying levels of adhesive resin 90%, 85% and 80% with a mixture of isocyanate and polyol 5%, 5%, 5%. This study aimed to obtain the value of toughness on the specimen composite polymeric foam powder and water hyacinth fiber, obtain mechanical behavior, knowing the effect of the composition of materials by impact testing standard ASTM E23-56T and get the best material composition to be used as a polymeric foam composite material. The results of impact testing method charpy shows that the toughness of the specimens highest obtained was 110.8 J / mm2, mechanical behavior demonstrated by the occurrence of fractures of the specimens from the impact pendulum during testing, material composition greatly affect the value of toughness specimens of composite and the composition of the best material to be made of composite materials is the water hyacinth powder with resin adhesive content of 90%.
Keywords: fiber / powder hyacinth, polymeric composites, impact test.

Filename:V8099 PENGARUH KOMPOSISI SERAT DAN SERBUK ENCENG.pdf
Filesize: 560.96 kB
Filetype:pdf (Mime Type: application/pdf)
Creator:admin
Created On: 01/01/2016 00:00
Viewers:Everybody
Maintained by:admin
Hits:868 Hits
Last updated on: 02/24/2016 12:15
Homepage:
CRC Checksum:
MD5 Checksum: